Upass Material Technology (Shanghai) Co.,Ltd.
| Thickness | 0.09-0.265 mm |
| Width | 900-1200 mm |
| Sleeve ID | 76 mm |
| Frictional Coefficient | ≥0.6 |
| Tensile Strength | ≥50 Mpa |
| Maximum Tension | ≥200 N/50mm |
| Elongation at Maximum Tension | ≥250% |
| Elongation at Break | ≥250% |
| Nail Rod Tear Strength | ≥60 N |
| Dimensional Stability | ≤1.5% at 90 ℃ |
| Tear Strength | ≥25 N |
| Heat Resistance | 70 ℃, 24h |
| Low Temperature Flexibility | -30 ℃, no cracks |
| Tensile Retention Rate | ≥90% |
| Elongation Retention Rate | ≥80% |
| Model Number | Strength Cross Laminated Film 60F |
| Brand Name | upasschina |
| Place of Origin | Shanghai, China |
View Detail Information
Explore similar products
Tapes Application MOPP Release Film MOPP UV Release Film Release Liner
MOPP Film MOPP Release Film MOPP Silicone Coated Release Liner
Good Light Transmission MOPP Release Liner With Smooth Surface
PP Silicone Coated MOPP Film Heat Resistant With Good Release Force
Product Specification
| Thickness | 0.09-0.265 mm | Width | 900-1200 mm |
| Sleeve ID | 76 mm | Frictional Coefficient | ≥0.6 |
| Tensile Strength | ≥50 Mpa | Maximum Tension | ≥200 N/50mm |
| Elongation at Maximum Tension | ≥250% | Elongation at Break | ≥250% |
| Nail Rod Tear Strength | ≥60 N | Dimensional Stability | ≤1.5% at 90 ℃ |
| Tear Strength | ≥25 N | Heat Resistance | 70 ℃, 24h |
| Low Temperature Flexibility | -30 ℃, no cracks | Tensile Retention Rate | ≥90% |
| Elongation Retention Rate | ≥80% | Model Number | Strength Cross Laminated Film 60F |
| Brand Name | upasschina | Place of Origin | Shanghai, China |
| High Light | High Strength MOPP Film ，Anti-Slip MOPP Film ，High and Low Temperature Resistance MOPP Film | ||
| Data Sheet | ||||||
| Item | Unit | Performance Index | ||||
| Thickness | mm | 0.09-0.265 | ||||
| Width | mm | 900-1200 | ||||
| Sleeve ID | mm | 76 | ||||
| Frictional Coefficient | / | ≥0.6 | ||||
| Tensile Properties | Tensile Strength | Mpa | ≥50 | |||
| Maximum Tension | (N/50mm) | ≥200 | ||||
| Elongation at Maximum Tension | % | ≥250 | ||||
| Elongation at Break | % | ≥250 | ||||
| Nail Rod Tear Strength | N | ≥60 | ||||
| Dimensional Stability at 90 ℃ | % | ≤1.5% | ||||
| Tear Strength | N | ≥25 | ||||
| Heat Resistance(70 ℃, 24h) | ℃ | After applying asphalt, the maximum curling of the polymer film or tire base edge shall not exceed 1/4 of the edge length | ||||
| Low Temperature Flexibility | ℃ | -30 ℃, no cracks, no layering | ||||
| Aging Test (70 ℃, 7days) | Appearance | No bubbles, no layering | ||||
| Tensile Retention Rate | % | ≥90 | ||||
| Elongation Retention Rate | % | ≥80 | ||||
| Q1: Are you trading company or manufacturer ? |
| A1: We are manufacturer. |
| Q2: Do you provide samples ? is it free or extra ? |
| A2: Yes, we could offer A4 sample for free charge but if you need in roll,we can offer 100-200m/roll for free, but shipping cost need you to paid. |
| Q3: How long is your delivery time? |
| A3: Depends on your quantity. Generally it is about 30 days for 20GP container. |
| Q4: How to pay for your goods? |
| A4: By L/C, by T/T (30% deposit before production, 70% balance before loading). |
Company Details
Business Type:
Manufacturer
Year Established:
2008
Total Annual:
50000000-80000000
Employee Number:
200~500
Ecer Certification：
Verified Supplier
UPASS, founded in 2008, is headquartered in New Materials Industrial Park, Qingpu District, Shanghai, and has two production bases in Taicang, Jiangsu and Chenzhou, Hunan. UPASS adopts European professional film manufacturing equipment and technology, mainly provides SDM strong cross film, var... UPASS, founded in 2008, is headquartered in New Materials Industrial Park, Qingpu District, Shanghai, and has two production bases in Taicang, Jiangsu and Chenzhou, Hunan. UPASS adopts European professional film manufacturing equipment and technology, mainly provides SDM strong cross film, var...
Get in touch with us
Leave a Message, we will call you back quickly!