3000 Cps Electronic Potting Silicone Encapsulants RTV184 Transparent

Product Specification

Electronic Potting Silicone Encapsulants RTV184 Transparent Silicone Electrical Potting Compound

Product Description

Silicone MCSIL-E184 is supplied as a two-component 10 to 1 liquid silicone addition cure system. Silicone MCSIL-E184 consists of Part A and Part B. When two components are thoroughly mixed, the mixture cures to a flexible elastomer, which is well suited for the protection of electrical/electronic applications.

Technical datasheet of Electronic Potting Silicone Encapsulates

Applications

Silicone is a general purpose compound suited for adhesive and coating. This cost-effective silicone can be used in a variety of electronic potting applications including the adhesive and coating for solar power, HID, LCD displayers, circuit board and electronic components, etc.

Features

Good Flow ability

Room temperature and heat cure

Good dielectric properties

Rapid, versatile cure processing controlled by temperature

High transparency allows easy inspection of components

Instruction :

Preparing Surfaces

In applications requiring adhesion, priming will be required for many of the silicone encapsulants. For best results, the primer should be applied in a very thin, uniform coating and then wiped off after application. After application, it should be thoroughly cured prior to application of the silicone elastomer.

Processing & Curing

MC Silicone E184 part A and Part B should be thoroughly mixed at a 10:1 ratio , may be poured/dispensed directly into the container in which it is to be cured. Care should be taken to minimize air entrapment. When practical, pouring/dispensing should be done under vacuum, particularly if the component being potted or encapsulated has many small voids. If this technique cannot be used, the unit should be evacuated after the silicone encapsulant has been poured/dispensed. MC silicone encapsulants may be either room temperature (25°C/77°F) or heat cured. Room temperature cure encapsulants may also be heat accelerated for faster cure. Ideal cure conditions for each product are given in the product selection table.

Pot life and curing rate

Cure reaction begins with the mixing process. Initially, cure is evidenced by a gradual increase in viscosity, followed by gelation and conversion to a solid elastomer. Pot life is defined as the time required for viscosity to double after base and curing agent are mixed and is highly temperature and application dependent. Please refer to the data table.

Useful Temperature Ranges

For most uses, silicone elastomers should be operational over a temperature range of -45 to 200°C (-49 to 392°F) for long periods of time. However, at both the low and high temperature ends of the spectrum, behavior of the materials and performance in particular applications can become more complex and require additional considerations and should be adequately tested for the particular end-use environment.

Precautions

1. The curing time varies due to different temperature, the higher temperature, it cures faster. Users can adjust the ratio of catalyst according to the temperature in order to get an ideal curing speed.
2. Certain materials can inhibit the cure of Silicone rubber. The most notable include: sulfur, polysulfide, sulfur-containing material, Organ tin and organ metallic compound, etc.
3. Prevent from contact with tin, phosphorus, water, ammonium, chlorine, carboxylic acid, hydroxyl compound, etc. to avoid un-curing circumstance.

Packing and Storage

1. Silicone rubber is shipped as kits that Part A and B liquid components in separate containers. It is available in packing in 5kg or 20kg,200kg per pail.

2. Silicone rubber must be tightly sealed in cool and dry place, prevented from sun and rain. Transport by non-dangerous goods.

Storage & Transportation of Electronic Potting Silicone Encapsulates

Keep it from strong sunshine, heat, and store in cool & dry place, well sealed. It has a shelf life of 12 months.It can be stroked and transported as non-dangerous goods.