Shenzhen Haneste New Material co.,LTD
| Payment Terms | T/T |
| Packaging Details | 25KG/ Iron Drum |
| Color | Grey,white, black (can be customized) |
| Sample | Can be offered |
| Temperature Resistance | -50~+250ºC |
| Thermal conductivity | Can be customized |
| Dielectric intensity | 18~25Kv/mm(25ºC) |
| Shelf life | 6 months |
| Appearance | Liquid |
| Mixing Ratio (A : B) | 1:1 |
| Viscosity | 4500~5000 |
| Hardness | 50±5 shore A |
| Brand Name | Hanast |
| Model Number | HN-8806 A/B (1:1) |
| Certification | ROHS，SGS |
| Place of Origin | Guangdong, China |
View Detail Information
Explore similar products
Hanast 10:1 Potting Compound Insulation And Moisture-Proof Potting AB Adhesive
Insulated Electrical Silicone Potting Compound Gel Flame Retardant Grey Liquid
Electronic Rtv Silicone Potting Gel Compound Flexible Adhesive Waterproof
LED Encapsulation Silicone Potting Compound Gel For Electrical Insulation
Product Specification
| Payment Terms | T/T | Packaging Details | 25KG/ Iron Drum |
| Color | Grey,white, black (can be customized) | Sample | Can be offered |
| Temperature Resistance | -50~+250ºC | Thermal conductivity | Can be customized |
| Dielectric intensity | 18~25Kv/mm(25ºC) | Shelf life | 6 months |
| Appearance | Liquid | Mixing Ratio (A : B) | 1:1 |
| Viscosity | 4500~5000 | Hardness | 50±5 shore A |
| Brand Name | Hanast | Model Number | HN-8806 A/B (1:1) |
| Certification | ROHS，SGS | Place of Origin | Guangdong, China |
| High Light | rtv potting Gel ，rtv potting Material ，RTV Silicone Gel Material | ||
Silicone Manufacturer Waterproof Silicone Potting Compound High Thermal Conductivity 1:1 Potting Glue Adhesive For Led Driver Power Module Battery Inverter
HN-8806 A/B (1:1)
HN-8806, two-component addition type silicone potting rubber which can be cured into high-performance elastomer by room temperature or heating
* Packing :
10KG / Set (A, 5kg + B, 5kg)
20KG / Set (A, 10kg + B, 10kg)
50KG / Set (A, 25kg + B, 25kg)
Product Features:
Excellent electrical insulation, high moisture resistance, and a wide temperature range of -50°C to 250°C.
Low-viscosity potting compound that Will cure in deep sections. Low shrinkage rate after curing,
will not emit heat and by-products, no corrosion for filling and sealing components
Good thermal conductivity
Technical Parameters:
| Test Items | Test Standard | Units | Product test results | |||
| Part A | Part B | |||||
|
Before Curing
| 1 | Appearance | By eyes | --- | Grey, fluid | White, fluid |
| 2 | Viscosity | GB/T10247- 2008 | 25ºC,mPa·S | 4500~5000 | 4500~5000 | |
| 3 | Density | GB/T 13354-92 | 25ºC,g/cm3 | 1.50±0.05 | 1.50±0.05 | |
| 4 | Mixing Ratio (A : B) | 1:1 | Weight ratio | 100 | 100 | |
| Volume ratio | 100 | 100 | ||||
| 5 | Operating time | Measured | hr | 0.3-0.4 | ||
| 6 | Curing condition | Measured | hr | 4~12 (25ºC, initial cure) | ||
| 0.20 (80ºC) | ||||||
| After Curing
| 7 | Appearance | By eyes | --- | Grey Elastomer | |
| 8 | Hardness | GB/T 531.1-2008 | Shore A | 50±5 | ||
| 9 | Thermal conductivity | GB/T10297-1998 | w/m·k | ≥0.76 | ||
| 10 | Expansivity | GB/T20673-2006 | µm/(m,ºC) | 210 | ||
| 11 | Moisture Absorption | GB/T 8810-2005 | 24h,25ºC,% | 0.01~0.02 | ||
| 12 | Volume resistivity | GB/T 1692-92 | (DC500V),Ω· cm | 1.0×1016 | ||
| 13 | Dielectric intensity | GB/T 1693-2007 | Kv/mm(25ºC) | 18~25 | ||
| 14 | Temperature Resistance | Measured | ºC | -50~+250 | ||
* UV-94 Fire retardant: After two times 10s burn tests on a 3mm-thick sample, the flame was extinguished within 30s, and no burnt fell. [1]
* Noted: The data after curing are all measured after the silicone is completely cured.
HOW TO USE
1. When used, weigh A and B according to proportion and then mix them evenly.
Mix thoroughly and evenly with a clean stirring device in a clean container, and then potting can be done.
It can also be sealed under a vacuum after removing the bubbles.
2. The surface of the potting element needs to be cleaned.
If the potting product is too large, it is recommended to potting in stages and then cure at room temperature (4-12hr) or by heating (80ºC-0.5hr).
3. For the automatic potting production line, in order to ensure accurate mixing ratio of A and B, Part A and Part B should be vacuumed respectively to remove the bubbles (the foaming time is 5-10 minutes), and then A and B should be pumped to the static mixer in proportion with a metering pump, and then potting can be done after mixing evenly.
Company Details
Business Type:
Manufacturer
Year Established:
2010
Total Annual:
5000000-10000000
Employee Number:
50~100
Ecer Certification：
Verified Supplier
Shenzhen Hanast New Polymer Materials Co., Ltd. was founded in 2010 and focuses on the development of new silicone materials. It is a national high-tech enterprise integrating the development, production, sales and service of silicone products. With an operation area of 16000 ㎡, our company has be... Shenzhen Hanast New Polymer Materials Co., Ltd. was founded in 2010 and focuses on the development of new silicone materials. It is a national high-tech enterprise integrating the development, production, sales and service of silicone products. With an operation area of 16000 ㎡, our company has be...