Multi Functional Acrylic Aliphatic Polyurethane Paint / Alkyd Oil Based Paint

Product Specification

Multi Functional Acrylic Aliphatic Polyurethane Paint / Alkyd Oil Based Paint

Acrylic Aliphatic Polyurethane Paint Introduction

Two-component polyurethane coatings have excellent film forming temperature, strong adhesion, good wear resistance, high hardness, good chemical resistance and weather resistance, and are widely used as industrial protection, wood furniture and automotive coatings. Waterborne two-component polyurethane coatings combine the high performance of two-component solvent-based polyurethane coatings with the low VOC content of waterborne coatings, making them a research hotspot in the coatings industry. The aqueous two-component polyurethane coating is composed of an -OH-containing aqueous polyol and a -NCO-based low-viscosity polyisocyanate curing agent, and its coating properties are mainly determined by the composition and structure of the hydroxy resin.

Acrylic Aliphatic Polyurethane Paint Feature

1. High decorative performance
2. Performance diversity, adjustability. Through the improvement of the formula, the polyurethane coating film can be made into a high hardness coating film, or can be made into an elastic coating film with excellent flexibility, which greatly enhances the application range of the polyurethane coating.
3. High temperature resistance and low temperature resistance.
4. The film is non-toxic after curing.
5. Environmentally friendly low voc coating

Polyurethane paint is polyurethane paint. It is strong in film, full of luster, strong adhesion, water resistant, abrasion resistant and corrosion resistant. It is widely used in high-grade wood furniture and can also be used on metal surfaces.
Characteristics of two-component polyurethane paint: Hydroxy-curable polyurethane paint has the advantages of being dry at room temperature, low toxicity, tough film, high gloss, good adhesion, corrosion resistance, oil resistance and water resistance. It is used in metal and cement. , wood and rubber, leather and other materials. Catalytic curable polyurethane lacquer coating has good oil, water, acid and alkali resistance, organic solvent resistance, and has good adhesion and wear resistance. It is generally used as a surface coating for wood, concrete, etc. Floor paint). Two-component polyurethane coatings generally consist of an isocyanate prepolymer (also known as a low molecular urethane polymer) and a hydroxyl-containing resin, commonly referred to as a curing agent component and a main component.

Two-component polyurethane coating advantage

1. Polyester lacquer is characterized by the formation of acyclic and/or circular hydrogen bonds between polymer molecules. Under external force, hydrogen bonds can be separated to absorb external energy (20~25kJ per mole of absorption). When the external force is removed, the hydrogen bond can be re-formed. Such a hydrogen bond cleaves and re-forms reversibly, making the polyurethane paint film highly mechanically wear resistant and tough. Compared with other paints, under the same hardness conditions, polyurethane paint film has the highest elongation at break due to hydrogen bonding, so it is widely used as floor paint, overtime paint, high decorative anticorrosive paint, and the like.
2. Some varieties of coatings (such as epoxy, chlorinated rubber, etc.) have good protection and poor decorativeness; some varieties (such as nitrocellulose lacquer) have good decorative properties and poor protection. However, polyurethane paint is both protective and decorative, and can be used for the coating of high-grade wood, piano, and large passenger aircraft.
3. the paint film has strong adhesion. Polyurethane, like epoxy, can be formulated as an excellent binder. Therefore, the coating film has excellent adhesion to a variety of surfaces (metal, wood, rubber, concrete, certain plastics, etc.). The author's experience is that for some metal surfaces, the adhesion of polyurethane paint is slightly inferior to that of epoxy paint; but for rubber, the polyurethane paint exceeds the epoxy paint.
4. the elasticity of the coating film can be adjusted according to the needs of the distribution ratio, can be adjusted from the extremely hard coating to the extremely flexible elastic coating, while the general paint such as epoxy, unsaturated polyester, amino alkyd, etc. can only It is difficult to impart high elasticity by making a rigid coating.
5. the coating film has excellent chemical resistance, acid, alkali, salt liquid, petroleum products, so it can be used as maintenance coating for drilling platforms, ships, chemical plants, and inner wall coating of petroleum storage tanks.
6. can be dried at high temperatures, but also can be cured at low temperatures. In a typical room temperature curing coating: epoxy, polyurethane, and unsaturated polyester, epoxy and unsaturated polyesters are difficult to cure below 10 ° C. Only polyurethane can be cured at 0 ° C, so the construction season long. Because it can be cured quickly at room temperature, it can be used for large-scale projects such as large oil tanks and large aircraft to achieve better performance than ordinary baking varnishes.
7. polyurethane paint can be made resistant to -40 ° C low temperature varieties. It can also be made into high temperature insulating varnish with properties close to polyimide.
8. The electromagnetic wire coated with polyurethane paint can be used for automatic assembly of tin in molten solder without scraping paint. It is especially suitable for the assembly of telecommunication equipment and instruments.

Product specifications

Expiration date - 12 Months

* A MSDS of the products is available on request.
Typical starting formulation for:
PU glossy finishes

PART A

LGalk 3-C880 Alkyd Resin 49%
Toluene 15%
Ethyl acetate 15%
Xylene 10%
Butyl acetate 10%
Silicone-free surface agent(BYK301) 1%

PART B

Desmsdur L-75 (Bayes) 64%
Toluene 11%
Butyl acetate 25%

Formula ratio
Part A / Part B = 2 / 1
NCO / OH = 1 / 1

Thinner

Toluene 10%
Xylene 30%
Ethyl acetate 10%
Butyl acetate 30%
Methoxyethyl acetate 20%