QINGDAO LAURENT NEW MATERIALS CO.,LTD
| Packaging Details | packed on wooden pallets, with water-proof cover, and tightened with plastic/steel bandages |
| Delivery Time | 20~30 days |
| Payment Terms | T/T;L/C |
| Supply Ability | 10000 ton/Year |
| Cold Crush Strength | 20-80Mpa |
| Application | high temperature industrial furnaces |
| Working Temperature | 1250-1350 |
| Creep Rate | less than 0.3% |
| Al2O3 Content | 70-90% |
| Processing Service | firing |
| Sio2 Content | less than 2% |
| Refractoriness Under Load | greater than 1500°C |
| Usage | industrial furnace |
| Thermal Shock Resistance | good |
| Raw Material | High Alumina Bauxite |
| Feature | Thermal Shock Resistance |
| Fe2O3 Content | less than 2% |
| Apparent Porosity | less than 22% |
| Thermal Conductivity | less than 2.5 W/m·K |
| Place of Origin | Zibo, China |
| Brand Name | Laurel |
| Certification | ISO9001 |
| Model Number | Laurel-03 |
View Detail Information
Explore similar products
Low Iron Content High Alumina Brick Refractory High Alumina Thermal Insulation
High Temperature Refractory Fireproof Insulation Thermal High Alumina Brick Low
Castable Cement Kiln High Alumina Brick Lightweight Refractory Brick For
High Temperature Fire Proof Hheater Thermal High Alumina Brick Lightweight
Product Specification
| Packaging Details | packed on wooden pallets, with water-proof cover, and tightened with plastic/steel bandages | Delivery Time | 20~30 days |
| Payment Terms | T/T;L/C | Supply Ability | 10000 ton/Year |
| Cold Crush Strength | 20-80Mpa | Application | high temperature industrial furnaces |
| Working Temperature | 1250-1350 | Creep Rate | less than 0.3% |
| Al2O3 Content | 70-90% | Processing Service | firing |
| Sio2 Content | less than 2% | Refractoriness Under Load | greater than 1500°C |
| Usage | industrial furnace | Thermal Shock Resistance | good |
| Raw Material | High Alumina Bauxite | Feature | Thermal Shock Resistance |
| Fe2O3 Content | less than 2% | Apparent Porosity | less than 22% |
| Thermal Conductivity | less than 2.5 W/m·K | Place of Origin | Zibo, China |
| Brand Name | Laurel | Certification | ISO9001 |
| Model Number | Laurel-03 | ||
| High Light | high alumina refractory brick ，high alumina cement | ||
Low Iron Content High Alumina Brick Higher Density Thermal Insulation
The most competitive price,good quality,safty packing,prompt delivery time,and excellent after-sales services.
Lower ferric Oxide,lower porosity,higher refractoriness,higher density,higher CCS and exact tolerance.
Specifications:
Ordinary High alumina brick
| Item | HA60 | HA70 | HA75 | HA80 |
| AL2O3(%) | ≥60 | ≥70 | ≥75 | ≥75-80 |
| SIO2(%) | 32 | 22 | 20 | ≥18 |
| Fe2O3(%) | ≤1.8 | ≤1.8 | ≤1.8 | ≤1.8 |
| Refractoriness °C | 1790 | ＞1800 | ＞1825 | ≥1850 |
| Bulk density,g/cm3 | 2.4 | 2.45-2.5 | 2.5 | 2.55-2.6 |
| Softening temperature under load | ≥1470 | ≥1520 | ≥1530 | ≥1550 |
| Apparent porosity,% | 22 | ＜21 | ＜21 | ＜20 |
| Cold Crushing strength Mpa | ≥45 | ≥50 | ≥54 | ≥60 |
Phosphate bonded high alumina bricks
| Item | LAP75 | LAP77 | LAP85 |
| AL2O3 % | ≥75 | ≥77 | ≥80-85 |
| Fe2O3 % | ≤3.0 | ≤3.0 | ≤1.8 |
| Ca0 % | ≤0.6 | ≤0.6 | ≤0.6 |
| Refractoriness °C | ≥1800 | ≥1800 | ≥1850 |
| Bulk density g/cm3 | ≥2.65 | ≥2.70 | ≥2.80 |
| Cold crushing strength MPa | ≥60 | ≥64 | ≥110 |
| Refractoriness under load 0.2MPa °C | ≥1350 | ≥1300 | ≥1350 |
| Application | Used for high temperature parts lining of cement rotary kiln | Used for Badly worn parts of cement rotary kiln | |
Description:
Laurel high alumina bricks are produced with selected bauxite chamotte by advanced process and strict quality control. The main mineral components are corundum and mullite phases. It features excellent high temperature mechanics and chemical corrosion resistance.
Features
1.Resisting high temperature
2.Great bulk density
3.Low iron content
4.Good eroding resistance
Applications:
1. Steel furnaces
2. Iron making furnaces
3. Glass kiln
4. Ceramic tunnel kiln
5. Cement kiln
Competitive Advantage:
Company Details
Business Type:
Manufacturer,Exporter,Trading Company,Seller
Year Established:
2003
Ecer Certification：
Site Member
QINGDAO LAURENT NEW MATERIALS CO.,LTD Established in 2003, and is situated in Qingdao City China, a city being a grand sea port in the world. Its professional Team has been in the field of refractory over 10 years. Exported to over 50 countries, built firm business relations with over 200 ... QINGDAO LAURENT NEW MATERIALS CO.,LTD Established in 2003, and is situated in Qingdao City China, a city being a grand sea port in the world. Its professional Team has been in the field of refractory over 10 years. Exported to over 50 countries, built firm business relations with over 200 ...
Get in touch with us
Leave a Message, we will call you back quickly!